STAINLESS A286 Forgings Pipes Tubes Bars Plates Sheets Strips Wires Rods

We are leading manufacturer and stockist of STAINLESS A286 in China. STAINLESS A286 Technical Data Sheet STAINLESS A286 is an iron-nickel-chromium alloy with additions of molybdenum and titanium. A 286 is one of the most popular high temperature alloys. As one of the austenitic alloys it...

We are leading manufacturer and stockist of STAINLESS A286 in China.

STAINLESS A286 Technical Data Sheet 

STAINLESS A286 Chemical Composition Limits

Weight%

C

Mn

P

S

Si

Cr

Ni

Mo

Ti

V

Al

B

Co

Cu

A286

0.08 max

2 max

0.025 max

0.025 max

1 max

13.5-16

24-27

1-1.5

1.9-2.35

0.10-0.50

0.35 max

0.0003-0.010

1 max

0.50 max

STAINLESS A286 is an iron-nickel-chromium alloy with additions of molybdenum and titanium. A 286 is one of the most popular high temperature alloys. As one of the austenitic alloys it maintains good strength and oxidation resistance at temperatures up to 1300ºF. Due to it's high strength and excellent fabrication characteristics A286 is used in various components of aircraft and industrial gas turbines. A286 is also widely used in the offshore oil and gas industry where the components are subject to high levels of heat and stress.

 

Alloy A286 bar can be solution treated at the temperatures detailed below, rapid cooled and then age hardened at 1325ºF (720ºC) for 16 hours and air cooling. The 1800ºF (980ºC) solution treatment produces the highest creep-rupture strength in age-hardened material whereas the 1650ºF (900ºC) treatment results in improved ductility and room temperature strength. If you require further information regarding A286 contact Sales.

   

STAINLESS A286 Solution Treated

A286 Solution Treated is covered by specification AMS 5731 (AMS 5732 Capable) and BS HR52

 

Solution Heat Treatment: 1800ºF ± 25 (982 ± 14ºC) 1 hour, water/oil quench (AMS)

Hardness: ≥ 217HB or 220 HB (BS), ≥201HB (AMS)

 

STAINLESS A286 Solution Treated and Aged (1800ºF)

 

STAINLESS A286 Solution Treated and Aged is covered by specifications AMS 5732, BS HR51, ASTM A638 660 Type 2, ASTM A453 660 Class B

 

Solution Heat Treatment:

980ºC ± 10 for > 1 hour, followed by air cool (BS)

1800ºF ± 25 (982 ± 14ºC) 1 hour, water/oil quench (AMS)

 

Precipitation Heat Treatment:

720ºC ± 10 > 16 hours, followed by air cool (BS)

1300-1400 ºF (704-760ºC) hold not less 16 hours, air cool (AMS)

 

STAINLESS A286Hardness:

248 - 341 HB or 260 - 360 HV (BS)

248-341 HB (AMS)

 

STAINLESS A286 Mechanical Properties

 

Alloy

0.2 Proof Stress (min)

Tensile Strength (min)

Elongation (min)

Alloy A286 Solution Treated and Aged (BS)

590 N/mm

900 N/mm

13%

Alloy A286 Solution Treated and Aged (AMS)

85 ksi (586 mpa)

130 ksi (896 mpa)

15%

 

A286 Solution Treated and Aged (1650ºF)

A286 Solution Treated and Aged is covered by specifications AMS 5737, ASTM A638 660 Type 1, ASTM A453 660 Class A and EN-2303 (under 4" Bar)

Solution Heat Treatment:

1650ºF ± 25 (899 ± 14ºC) 1 hour, water/oil quench (AMS)

Precipitation Heat Treatment

1300-1400 ºF (704-760ºC) hold not less 16 hours, air cool (AMS)

Hardness

277-363 HB (AMS)

 

STAINLESS A286 Mechanical Properties

Alloy

0.2 Proof Stress (min)

Tensile Strength (min)

Elongation (min)

Alloy A286 Solution Treated and Aged (AMS)

95 ksi ( 655mpa)

140 ksi (965 mpa)

12%

 

A286 Other

AMS 5853 - 15% cold reduced (160 ksi/ 1103 Mpa tensile strength)

AMS 5726 - 40-50% cold reduced (200 ksi/ 1379 Mpa tensile strength)

 

STAINLESS A286 Specifications

AMS 5525 Sheet / Stirp / Plate

AMS 5723 (cancelled)

AMS 5726 Bar Work Str 200ksi min

AMS 5731 Bar 1800°F Sol Trtd

AMS 5732 Bar 1800°F Sol Trtd /Aged

AMS 5734 Bar 1650°F Sol Trtd

AMS 5737 Bar 1650°F Sol Trtd /Aged

AMS 5853 Bar Cold Red 160ksi min

AMS 5858 Sheet / Strip (welding gr)

AMS 5895 Bar

ASTM A638 660 Type 1

ASTM A638 660 Type 2

ASTM A453 660 Class A

ASTM A453 660 Class B

BS HR51 Bar 1800°F Sol Trtd /Aged

BS HR52 Bar 1800°F Sol Trtd

BS HR650

AECMA PrEN 2171

AECMA PrEN 2119

AECMA PrEN 2172

AECMA PrEN 2173

AECMA PrEN 2303

AECMA PrEN 2304

AECMA PrEN 2398

AECMA PrEN 2399

AECMA PrEN 3510

AECMA PrEN 2175

AECMA PrEN 2417

ws 1.4980

UNS S66286

 

 

The STAINLESS A286 items which we can manufacture and supply are the followings.

STAINLESS A286 Rod

STAINLESS A286 Rings

STAINLESS A286 Forgings

STAINLESS A286 pipe

STAINLESS A286 tube

STAINLESS A286 bars

STAINLESS A286 plates

STAINLESS A286 sheets

STAINLESS A286 Strip

STAINLESS A286 wire

STAINLESS A286 fitting Union

STAINLESS A286 Pipe Elbows

STAINLESS A286 PIPE Tee

STAINLESS A286 ADAPTERS

STAINLESS A286 pipe bend

STAINLESS A286 reducers

STAINLESS A286 fitting caps

STAINLESS A286 pipe outlets

STAINLESS A286 Stub Ends

STAINLESS A286 Couplings

STAINLESS A286 pipe Nipples

STAINLESS A286 BUSHINGS

STAINLESS A286 pipes sockets

STAINLESS A286 Pipe Gasket

STAINLESS A286 pipe joints

STAINLESS A286 pipe Cross

STAINLESS A286 Pipe Wyes

STAINLESS A286 seal ring

STAINLESS A286 Flange

STAINLESS A286 bolts

STAINLESS A286 nuts

 

ONE OF THE KIND, MILLIONS OF CHOICES

SUPERIOR QUALITY

PROMPT DELIVERY

FAVORABLE FEEDBACK

ALL AVAILABLE IN SMICO

SELECT SMICO, YOU WILL BE RIGHT

 

For more info and price of STAINLESS A286, please send us inquiry and you will have quick reply soon.


Hot Tags: STAINLESS A286 Forgings Pipes Tubes Bars Plates Sheets Strips Wires Rods,Stainless Steel