3d Printing Spherical Powder Mp35n Forgings Pipes Tubes Bars Plates Sheets Strips Wires Rods

We are leading manufacturer and stockist of MP35N in China. MP35N Technical Data Sheet MP35N is a multi-phase alloy containing Nickel, Cobalt, Chromium and Molybdenum with a unique range of properties - ultra high strength, toughness, biocompatibility and corrosion resistance. It is produced by...

We are leading manufacturer and stockist of MP35N in China.

 

MP35N Technical Data Sheet

MP35N Chemical Composition Limits

Weight %

Ni

Co

Cr

Mo

Ti

Fe

Si

Mn

P

B

S

C

MP35N

33-37

Bal

19-21

9-10.5

1 max

1 max

0.15 max

0.15 max

0.015 max

0.010 max

0.010 max

0.03 max

MP35N is a registered trademark of SPS Technologies Inc.

MP35N is a multi-phase alloy containing Nickel, Cobalt, Chromium and Molybdenum with a unique range of properties - ultra high strength, toughness, biocompatibility and corrosion resistance. It is produced by vacuum induction melting and vacuum arc re-melting (VIM-VAR) and is then strengthened by work hardening and aging, giving hardnesses of up to 55-60 Rockwell C and strength levels as high as 260-300KSI.

Due, to this unique combination of properties, MP35N has many applications in such industries as oil and gas, aerospace and medical. MP35N can be effectively used at cryogenic temperatures without embrittlement and maintain its properties at temperatures up to 600F, and is also suitable for medical implants and orthodontic/prosthetic devices.

MP35Nis able to resist corrosion to most mineral acid, hydrogen sulfide and seawater environments whilst exhibiting excellent resistance to stress corrosion cracking and hydrogen embrittlement, even at high strength levels. NACE MR0175 allows a hardness of up to 51 HRC for material that has been work strengthened and aged by one of the processes listed in the table below.

Aircraft Materials supplies MP35N in round bar certified to either AMS 5844 (0.270" - 1.520" diameter) or NACE MR0175 (0.5" - 2.5" diameter), as well as sheet, strip and plate products suitable for medical applications.

MP35N Mechanical Properties

Material

Condtion

Ultimate Tensile Strength ksi

0.2 % Yield Strength ksi

Elongation %

Reduction of Area %

Hardness HRC

MP35N
AMS 5844

Solution Heat Treated and Work Strengthened

255

225

12

50

45

MP35N
AMS 5845

Solution Heat Treated and Work Strengthened and Aged

260

230

8

35

38 min

AMS 5844 is Solution Treated and Cold Worked. The AMS specification only requires that the hardness shall not be lower than 38 HRC or equivalent. However other typical mechanical properties of AMS 5844 are detailed above.

Material

Condtion

Tensile Strength ksi

Yield Strength ksi

Elongation %

Reduction of Area %

Hardness HRC

MP35N
NACE MR0175

Age @ 1300F/ 4 hrs

220

210

10

40

51 max

MP35N
NACE MR0175

Age @ 1350F / 4hrs

210

200

10

40

51 max

MP35N
NACE MR0175

Age @ 1425F / 6hrs

190

180

10

40

51 max

MP35N Properties as per NACE MR0175 - Cold Drawn - Reduced Strength (min properties, round bar under 2" dia)

MP35N Specifications
UNS R30035

AMS 5758 - MP35N VIM-VAR Bar
Solution heat treated @1900-1925 F for 4 to 8 hours

AMS 5844 - MP35N VIM-VAR Bar
Solution heat treated @1900-1925F for 4 to 8 hours and Work Strengthened

AMS 5845 - MP35N VIM-VAR Bar
Solution heat treated @ 1900-1925F for 4 to 8 hours, Work Strengthened & Aged @ 1000-1200F for 4 hours

NACE MR0175
ASTM F-562 - Surgical Implant Applications
BS 7252-6 Surgical Implant Applications
ISO 5832-6 Surgical Implant Applications

Alloy MP159

AMS 5841

UNS R30159

AMS 5841 Bar (Solution Heat Treated)

Solution Heat Treat: 1900°F - 1925°F / 4-8 hours + Water Quench

AMS 5842 Bar (Solution Heat Treated and Work Strengthened)

Solution Heat Treat: 1900°F - 1925°F / 4-8 hours + Water Quench

Followed by work strengthened / strain hardening

 

AMS 5843 Bar (Solution Heat Treated, Work Strengthened and Aged)

Solution Heat Treat: 1900°F - 1925°F / 4-8 hours + Water Quench

Followed by work strengthened / strain hardening

Ffollowed by ageing: 1200-1250°F 4-4.5 hours + Air Cool.

 

The MP35N items which we can manufacture and supply are the followings.

MP35N Rod

3D printing spherical powder MP35N

MP35N Rings

MP35N Forgings

MP35N pipe

MP35N tube

MP35N bars

MP35N plates

MP35N sheets

MP35N Strip

MP35N wire

MP35N fitting Union

MP35N Pipe Elbows

MP35N PIPE Tee

MP35N ADAPTERS

MP35N pipe bend

MP35N reducers

MP35N fitting caps

MP35N pipe outlets

MP35N Stub Ends

MP35N Couplings

MP35N pipe Nipples

MP35N BUSHINGS

MP35N pipes sockets

MP35N Pipe Gasket

MP35N pipe joints

MP35N pipe Cross

MP35N Pipe Wyes

MP35N seal ring

MP35N Flange

MP35N bolts

MP35N nuts

 

ONE OF THE KIND, MILLIONS OF CHOICES

SUPERIOR QUALITY

PROMPT DELIVERY

FAVORABLE FEEDBACK

ALL AVAILABLE IN SMICO

SELECT SMICO, YOU WILL BE RIGHT

 

For more info and price of MP35N, please send us inquiry and you will have quick reply soon.