Anti- Heavy Corrosion, High Waterproof, Anti-fire, High Durability Materials

Anti- Heavy Corrosion, High Waterproof, Anti-fire, High Durability Materials

Anti- heavy corrosion, high waterproof, anti-fire, high durability materials H igh W aterproof New Materials Product Features: 1. Super adhesion, low temperature softness, high temperature resistance and excellent physical properties; 2, excellent impact resistance, wear resistance, elasticity...

Chat Now

Anti- heavy corrosion, high waterproof, anti-fire, high durability materials

 01.png

02.png 

 

High Waterproof New Materials 

Product Features:

1. Super adhesion, low temperature softness, high temperature resistance and excellent physical properties;

2, excellent impact resistance, wear resistance, elasticity and high dense film properties;

3. Excellent corrosion resistance, salt spray resistance and seawater resistance;

4. Excellent weather resistance, heat resistance, cold resistance and water resistance;

5, No benzene solvents, no coal tar components, it is an environmentally friendly material;

6. Cold construction and construction are safe and convenient.

 Application areas:

Railway, tunnel, cavern, bridge waterproofing and other plugging projects;

Various military projects, water projects, nuclear power plants, subways, oceans, ships and docks and other difficult waterproof projects;

The senior engineering waterproof and special waterproof, moisture-proof projects;

Fill all kinds of irregular joints, cavities, seams, cracks; construction joints, expansion joints, culverts, swimming pools, reservoirs, sewage treatment works and other cracks in the concrete buildings.

Before and after comparison of insoluble leakage project

03.png

The insoluble leakage project site video


04.png

    After settled leakage project site   

Product Features:

TEST REPORT

Items

Test contents

Actual test value

1

Tensile Strength (MPa, 7d)

2

Tensile Strength (MPa, 14d)

22.1

2

Elongation at break (%, 7d)

122

Elongation at break (%, 14d)

611

3

Tear strength (N/mm, 7d)

12

4

Low temperature bending

No crack, @-40℃

5

Impervious(0.3MPa, 30mins)

impermeable

6

Solid content, %

99

7

Surface drying time, h

3

8

Actual drying time, h

24

9

Wet base bond strength (MPa, 7d)

0.50

10

Alkali resistance, with CA(OH)2 saturation by 500 hours

No cracking, No skin

Not falling off

11

Extension aging

Heat aging

No crack, No deformation

Artificial weathering

No crack, No deformation

12

Heat treatment, 7d

Tensile strength retention,%

105

Elongation at break,%

89

Low temperature bending, ℃

No crack, @-35℃

13

Alkali treatment, 7d

Tensile strength retention,%

60-150

Elongation at break,%

88

Low temperature bending, ℃

No crack, @-35℃

Alkali treatment, 14d

Tensile Strength, MPa

19.1

Elongation at break,%

485

14

Acid treatment, 7d

Tensile strength retention,%

107

Elongation at break,%

128

Low temperature bending

No crack, @-35℃

15

Artificial weathering

720h

No crack

No deformation

Product Features:

TEST REPORT

Items

Test contents

Standard value

Actual test value

Results

1

Tensile Strength, MPa

1.9

2.8

GOOD

2

Elongation at break,%

550

577

GOOD

3

Tear strength (N/mm)

12

15

GOOD

4

Low temperature bending

-40

-41

GOOD

5

Impervious (0.3MPa, 30mins)

impermeable

impermeable

GOOD

6

Solid content, %

80

95

GOOD

7

Surface drying time, h

12

5

GOOD

8

Actual drying time, h

24

23

GOOD

 VANS TECH" Heavy Anti-Corrosion New Materials 

Features:

Excellent corrosion & wearesistance, elasticity, and is resistant to high and low temperature, low temperature softness, shockproof, waterproof, soundproof and higher strength.

Application scope 1: metal and non-metal anti-corrosion, concrete base protection. Such as: offshore equipment facilities, offshore steel structures, marine concrete buildings;

Anti-corrosion in harsh environments, such as: smelting plants, battery plants, power plants and other acid and alkali environment; For gas pipelines, chemical plants, chemical equipment, non-metallic storage tanks, wooden objects, etc.

Scope 2: Metallurgy, chemical industry, ship, container, railway bridge, etc., to protect against atmospheric, seawater, oil and other chemical media.

Product Use: Widely used in heavy-duty anti-corrosion projects in the smelting industry, ocean, construction, power plants, petrochemicals, etc. It is suitable for marine and port concrete protection, surface protection of various ships and ships, as well as difficult anti-corrosion field in harsh environment (acid, alkali, salt spray salt water environment), also used in mine pipelines for wear protection, etc. The surface of the object is generally used for the intermediate layer and surface protection. Beautiful, comfortable, safe and durable.


Technical Indicators:

TEST REPORT

Test contents

Test value

Standard value

Shore hardness

65-90 (as clients requirements)

GB/T 2411

GB/T 529

GB/T 1768

GB/T 19250

GB/T 1720

GB/T 16777

Tensile strength (7d, MPa)

10.4

Tear strength (N/cm)

100

Wear resistance

(1,000 rpm, 1,000g), g

0.0040

Elongation,%

234

Adhesion

Grade 2

Film drying time, h

Surface drying time

1

Actual drying time

24

Bonding to the concrete drying interface (7d)

3.5 MPa

Bonding to concrete wet interface (7d)

2.4 MPa

8-shaped forming bonding,

7d MPa

2.1

Distilled water resistant, 90d

Normal

GB/T 1733

Hydrofluoric acid resistant, 24h

No bubble, Not falling off

Slight discoloration

GB/T 17657

Acid resistant(10%HCl, 10% sulfuric acid and 10% Nitric acid), 12months

No bubble, Not falling off

No discoloration

GB/T 1763

Alkali resistance (5% NaOH),  3,000h

No bubble, Not falling off

No discoloration

Resistant heat salt water(3%NaCI,40) 3,000h

No bubble, Not falling off

No discoloration

Salt spray resistance 3,000h

No bubble, Not falling off

No discoloration

GB/T 1771

Heat and humidity resistance≥3,000h

No bubble

Not falling off

GB/T 1740

Resistant super aqua regia 12months

No bubble

Not falling off

Note: 15% Sulfuric acid

15% Nitric acid

15% hydrochloric acid

“VANS TECH” High Fireproof New Materials 

It is a solvent-based fireproof material, a new organic synthetic material. It expands rapidly in case of fire, spread densely fire-proof and heat-insulating carbonized layers to protect the wooden, steel or other materials structures in the fire, prevent the buildings to collapse.

Product performance:

(1) Bond strength: 1.51 MPa.

(2) Water resistance: After soaking for 24 hours, the coating has no delamination and peeling off.

(3) Resistance to cold and heat cycle: After 15 thermal cyclings, the coating is free from chalking, cracking, flaking and foaming.

(4) Drying time: Surface drying time ≤ 8 hours, actual drying time 24 hours.

(5) Initial dry crack resistance: no cracks.

Fire Performance:

According to GB14907-2002 standard, MCC-FYM520 fireproof material is sprayed on 36B I-beam and loaded with 136KN. The experimental results are as follows:

TEST REPORT

Coating thickness, mm

0.59

1.1

1.7

2.18

3.01

refractory limit, h

0.5

1.0

1.5

2.0

2.5(Note: Fire resistance and coating thickness are subject to inspection report)


 “VANS TECH” Anti-High Temperature & Corrosion Materials

Features:

Anti corrosion & high temperature ≤ 600 °C; It is the best choice for petrochemical device use;

Excellent wettability, shielding, anti-rust, anti-corrosion,resistant to rain and water, superior high temperature resistance. When used outdoors longer, it will not be powdered or peeled off.

Application range:

Anti-corrosion and protection of the petroleum industry,chemical industry, and high temperature equipmen

Product Performance Index:

TEST REPORT

Items

Test contents

Actual test value

1

Color

Silver gray (any color)

2

Gloss

Matt

3

Density

1.02g/cm3

4

Volatile organic constituents (VOC)

195g/liter

5

Adhesion (Cross-cut method)

Grade 1

6

Flash point

27℃

7

Impact strength

≥ 50kg, cm

8

Temperature resistance

From -25℃ to 600℃

9

Wear resistance (700g/500r)

11.5 mg

10

Acid resistance, 30d

15% H2SO4

No corrosion, No bubble

Not falling off

 

7% HCl

11

Alkali resistance (30% NaOH),  30d

12

Salt resistance 60g/L, 30d

13

Salt spray resistance 2,000h

14

Oil resistance (No. 0 diesel, crude)

15

Recommended dry film thickness

20-40 Micron

16

Theoretical spread rate

50g/m2

17

Actual spread rate

The appropriate loss factor should be considered

18

Drying time

Surface drying time

1-3h

Actual drying time

24h

19

Coating interval

From 3h-48h

 


Hot Tags: Anti- Heavy Corrosion, High Waterproof, Anti-fire, High Durability Materials,New Materials And New Technology